FJ-C600 Series Fluorocarbon Coatings at Room Temperature
Introduction:
It overcomes the limitation of not being solidified at room temperature by previous fluorocarbon coatings on the basis of keeping the excellent performance by Shanghai Fuleda Fluorocarbon Material Co., Ltd., thus making the fluorocarbon coating be applicable to a lot of materials’ surface and widely expand its application based on reasonable supporting. It is a kind of super- weatherability coating like PVDF after being used and tested at home and abroad for almost twenty years.
FJ-C600 series fluorocarbon coatings are mixed by excellent fluorothene vinyl ether copolymer FEVE fluorocarbon resin, strictly selected pigments and extenders with weatherability, acid and alkali resistance, imported aluminum powder, pearl essence, auxiliary agent and solvent as well as supporting compounding agent with double packages, namely, package A and package B.
Application Fields:
Building Field:
It is applied to all kinds of building materials such as roof(various metal materials), door window, steel construction, various concrete, gas bell, cement roof tile, gate and druids altar etc.
Large-scale Fixtures:
It is applied to bridge, port facilities in large size, oil tanker, container and various marine facilities ect.
Traffic Field:
It is applied to automobile, locomotive, vehicle, airplane, ship, underground etc.
A Variety of Outdoor Building Fields:
It is applied to road sign and billboard, indicator board, handrail, store, highway guardrail, various outer plates for solar energy facilities, heat collecting pipe, exterior material for greenhouse, outdoor lamp shade etc.
Furniture Field:
It is applied to table, chair, floor and cupboard etc.
Home Appliance Field:
It is applied to refrigerator, TV, computer, washing machine, ice cuber, small home appliance etc.
Applicable Materials
Inorganic material (cement, concrete, asbestos, gypsum)
Metal material (cast and forged part, steel plate, copper plate, aluminium sheet, stainless steel)
Organic material (PVC plastic, ABS plastic, hardboard, plywood, timber)
Ceramics (ceramic tile, mosaic, pottery sand, keramics, porcelain etc.)
Glass material (polished glass, obscured glass)
Stone material (granite, marble, white marble etc.)
Performance:
■ Super-weatherability
Demonstrated by long-term use in the open air and accelerated weathering test, fluorocarbon bond of fluorocarbon resin molecule chain of FJ-C600 series fluorocarbon coatings can resist ultraviolet’s degradation, and compare favorably with hotsetting polyvinylidene fluoride fiber PVDF in terms of super-weatherability with outdoor service life no less than twenty years.
■ Super Corrosion and Chemical Resistance
FJ-C600 series fluorocarbon coatings can pass 3,000 hours of neutral salt spray test when painted on aluminium alloy and 1,000 hours of test when painted on galvanized steel. Its acid resistance is as excellent as that of hotsetting polyvinylidene fluoride fiber fluorocarbon coating, and the alkali resistance shall surpass the latter’s. In addition, the purpose of corrosion preserva- tion decoration of keelson for more than several decades can be achieved through multicoat and the decoration, shielding effect, corrosion inhibition and catelectrode of each coat.
■ Stain Resistance
It is characterized by exterior lubricity, low adhesiveness and not easy to be contaminated (easy cleaning if contaminated).
■ Excellent Workability
It can be coated on site with various ways like spray coating, roller coating and brush coating etc. What’s more, it can tightly adhere to nearly all materials in good condition with excellent adhesion and hardness. FJ-C600 series fluorocarbon coatings can preserve for many years if being coated for once. A lot of maintenance cost and scaffold building and removing charge can be saved because of easy maintenance. It is only required to clean the surface with water and paint top coating if recoating is needed.
■ High Decoration
FJ-C600 series fluorocarbon coatings can be used to match various colors like solid color, metallic color, pearlylustre color, photoluminescence, fluorescence color and glistening color as well as low, moderate and high lustre, thus presenting ample imaginary space and fantastic decorative effect for designers and owners.
■ Temperature Resistance
The coverage coated by FJ-C600 series fluorocarbon coatings can be used within -40℃-150℃.
Process Parameter:
Name |
Top coat |
Finish coat |
Product No. |
FJ-C600 |
FJ-C600 |
Appearance |
Dispersion in various colors |
Sub-transparent dispersion |
Fineness |
≤40μm |
﹤25μm |
Solid content(Wt%) |
≥50%(light color) 35%(metal) |
≥35 |
percentage of coverage(theory) |
16㎡/㎏on the condition of 20μm photopolymer |
22㎡/㎏ on the condition of 12μm photopolymer |
Curing condition |
Room temperature |
Room temperature |
Curative formula |
10/1 |
10/1 |
Thinner |
X-6 Thinner |
X-6 Thinner |
Coat Performance:
Performance and quality |
Standard |
FJ-C600 series fluorocarbon coating performance |
Base material |
Metal, concrete, ceramic tile, glass, synthetic fiber, hardboard, and plywood |
|
Color |
Various colors like solid, metallic color, and pearlylustre color |
|
60℃ luster |
GB/T 9754-1988 |
low, moderate and high luster |
Film thickness(photopolymer) |
Top coat 20-25μm, finishing coat10-15μm |
|
Pencil hardness(graze) |
GB/T 6739 |
Minimum2H |
Adhesion, degree |
GB/T 9286-1998 |
≤1 |
Impact resistance,cm |
GB/T 1732-1993 |
≥40 |
Temperature resistance |
-40-150℃ |
|
Resistance to solvent |
Xylene |
>100times without appearance of grounding |
Salt fog resistance |
GB/T 1771-1991 |
Up to standard or surpass standard in 1,000 hours |
Acid resistance(168h) |
GB/T 9274-1988 |
Normal |
Alkali resistance(168h) |
GB/T 9274-1988 |
Normal |
Water resistance(24h) |
GB/T 1733-1993 |
Normal |
Hot-cool-heat cycling resistance(168h) |
JG/T 25 |
Normal |
Fouling resistanc |
Pass |
|
Stain resistance |
GB/T 9757-2001,A |
≤10% |
Resistance to wet heat |
GB/T 1740-1989 |
Up to standard or surpass standard in 1,000 hours |
Washability, each time |
GB/T 9266-1988 |
>10000 |
Weathering resistance |
GB/T 1865-1997 |
Luster loss shall be less than 30% in 3,000 hours Color variation shall be no more than 5NBS |
Notice on Application:
Appropriate supporting system shall be selected and corresponding preliminary treatment be done according to your actual demand. No application when ambient temperature ≤5℃ and relative humidity ≥85%.
Coating formulation
It shall be allotted in accordance with prescribed proportion in the specification so as not to affect application and film coating quality. It is better to be used after twenty minutes’ curing. Do not prepare too much because the rest coating will get colloidized if not being used in time and the rest can not be placed in the original package. In addition, it is suggested to use supporting thinner to avoid affecting the appearance and quality of the film coating.
Film Coating Curing
Film coating shall become full curing in seven days after application and not expose to water in twenty-four hours after application. It is preferred to be used after full curing
Package and Supply:
Package:
Base coat, top coat, finish coat |
20㎏/barrel |
Thinner |
16㎏/barrel |
Supply:
There is no order quantity for base coat, finishing coat, thinner and top coat of Fuleda Color Card. The minimum supply of top coat monocolor ordered by other companies shall be 20 kg, and the general supply term is within two to five days (excluding transportation).
FJ-C600 series fluorocarbon coatings is widely applicable, with different supporting plans and notices in different application areas and materials. Please see Application Process Explanation of Shanghai Fuleda Fluorocarbon Material Co., Ltd. for particular process.