Shanghai Fulda Fluorocarbon Material Co., Ltd. is one of the most professional manufacturers of fluorocarbon materials in China.

+
  • 产品导入 (5)/image/nlvEtAkrRLinJAHT5VEgJw.jpg

BJ-C200 Series Room Temperature Acrylic Acid Polyurethane Coatings

Description

Introduction:

BJ-C200 series room temperature acrylic acid polyurethane coatings, a kind of cold curing coating, are confected from high quality hydroxy-acrylic resin, modified resin, isocyanic ester without yellow change, weathering resistance pigment and filling (tinting pigment and extender pigment), accessory ingredient, solvent by Shanghai Fuleda Fluorocarbon coating Fluorocarbon Material Co. Ltd.. It is packed in two components, namely component A and component B.

Application Fields:

Inorganic materials (Cement, concrete, asbestos and gypsum)

Metallic materials (tinplate, steel plate, aluminium plate, and stainless steel)

Organic materials (PVC plastic, ABS plastic, hardboard, plywood, wood)

Glass materials (polished glass, obscured glass)

Widely used in the outdoor protection and interior decoration for various building 

engineering (houses, apartment, office building and factory storage etc.)

Technological Parameters:

Name Base coat

Top coat

Finish coat

Product No.

BJ-C200A

BJ-C200

BJ-M200B

Appearance

White and light grey

Colors of all kinds

Transparent color

Fineness

≤30μm

≤35μm

≤25μm

Solid content(Wt%)

≥50%

≥50%(light color)

35%(metallic color)

≥35

Drying time

表干≤1h,实干≤24h

Mixing proportion (A: B)

10:1

Working life

8 h

Thinner

X-6 thinner

 

Coatings Performance:

Performance and quality

Standard

Performance Acrylic Acid and Polyurethane Coating

Base material

 

Mental, concrete, ceramic tile, glass, synthetic fiber, Hardboard and plywood

Color

 

Various colors like solid color pearlylustre color, and metallic color

luster

GB/T 9754-1988

Low, moderate and high luster

Film thickness(photopolymer)

 

Top coat 20-25μm,finishing coat 15-25μm

Hardness(pencil)

GB/T 6739

Minimum H

Adhesion

GB/T 9286-1998

100/100

Impact toughness resistance

GB/T 1732-1993

No motion

Temperature resistance

 

-40-150℃

Resistance to solvent

Xylene

100times without appearance of grounding

Salt-spray resistance

GB/T 1771-1991

-40-150℃

Acid resistance

GB/T 9274-1988

10%HCL15min making no difference

20% sulfuric acid 18h making no difference

Alkali resistance

GB/T 9274-1988

10%NaOH 1h making no difference

Resistance to laundering

GB/T 1733-1993

making no difference

Weatherability
(Sunlight acceleration)

GB/T 1865-1997

Luster loss less than 30% in 1000 hours

Color variation no more than 2NBS

 

Material, Color and Texture:

The main film-forming resin of BJ-C series resin coating adopts high quality acrylic acid and polyester resin.

Weathering resistance inorganic pigment, import metallic and pearlescent pigment which are also applicable to FJ-C is adopted.

At present, BJ-C200 series resin fluorocarbon coatings have solid color, metallic color, pearly color and color with other different gloss.

Packing and Supply:

Package:

Base coat, top coat, finish coat

20kg/barrel

Thinner

16kg/barrel

 

Supply:

The order quantity for top coat, finishing paint, thinner, whose color is based on the color chart from Shanghai Fuleda Fluorocarbon Material Co., Ltd., are not specified. The minimum monochromic supply for top coat ordered based on other companies sample is 20kg, and the delivery time of BJ-C200 Series Resin Coating is usually 2-5 days.