BJ-M210 Series High Temperature Acrylic Coatings
Product introduction:
BJ-M210 series high temperature acrylic coating is a baking cross-linking coating prepared by Shanghai Fulda Fluorocarbon Material Co., Ltd. using thermosetting hydroxy acrylic acid, amino resin, modified resin and weathering filler, auxiliary agent and solvent.
Application areas:
Phosphate, electroplating, aluminum, coated aluminum, coated steel, aluminum, high-end bicycles, electric bicycles, electronic housings, etc., coated aluminum, coated steel, aluminum profiles.
Performance characteristics:
■ Excellent weather resistance
Outdoor use 5-10 years
■ Highly decorative
It can be adjusted with various colors such as solid color, pearl color and metallic color, and various low, medium and high gloss. High hardness and full film
■ Excellent corrosion resistance and chemical resistance
■ Excellent construction performance
Can be sprayed by hand, electrostatically sprayed, recoating performance is good, curing temperature can be 180 °C12-12min or 130-150 °C20-30min
Process parameters:
| Product name | Primer |
Paint |
Cover paint |
|
Product number |
BJ-M210A |
BJ-M200 |
BJ-M200B |
|
Exterior |
White light gray |
Various colors |
Transparent |
|
Fineness |
≤30μm |
≤30μm |
≤25μm |
|
Viscosity (coating-4/S) |
≥80 |
≥80 |
≥60 |
|
Solid content |
≥50% |
≥50%(Light color) 35%(metal） |
≥35 |
|
Thinner |
X-4 Thinner |
X-4 Thinner |
X-4 Thinner |
|
Spray viscosity (25°CS) |
16-18 |
16-20 |
16-18 |
Performance:
|
Project |
Adopt standard |
BJ-M amino acrylic coating performance |
|
Color uniformity |
Various colors with pearly, solid, metallic luster |
|
|
Mirror gloss |
ASTMD-523 |
Low Medium High |
|
Film thickness (dry film) |
ASTMD-1400 |
Primer 8-15μm Topcoat 20-25μm Cover light 15-20 |
|
Hardness (pencil） |
ASTMD-3363 |
H-3H |
|
Adhesion scribing |
Dry adhesion Wet adhesion Adhesion after boiling water |
100/100 100/100 100/100 |
|
Impact toughness |
ASTMD-2794 |
The film does not move on the substrate |
|
Solvent resistance |
MEK test |
＞100 Times not exposed |
|
Wear resistance |
ASTMD-968 |
Exceeding the standard 40min |
|
Chemical resistance Hydrochloric acid resistance Resistant to mortar Nitrification resistance Washing resistance |
10% hydrochloric acid drip 24-hour cement block 70% HN03 steam 3%38°C72 hours |
no effect no effect No more than 5E unit change no effect |
|
Corrosion resistance Moisture resistance Salt spray resistance |
ASTMD-2247 ASTMD-117 |
500 hours to meet or exceed the standard requirements 500 hours to meet or exceed the standard requirements |
|
Weather resistance (daylight acceleration) |
|
1000 hours gloss loss is less than 30%, Color change is not greater than 5NBS units |
Use standards and quality assurance:
The production and inspection of BJ-M210 series resin coatings adopts the standard of American Building Aluminum Association AAMA2603.
BJ-M210 series resin coating raw materials, color and texture
BJ-M210 series resin coating main film-forming resin is made of high quality acrylic and polyester resin.
The pigments are all made of high weather resistant inorganic pigments, imported metals and pearlescent pigments suitable for FJ-C.
BJ-M210 series resin fluorocarbon coatings are currently available in solid, metallic, pearlescent and other gloss coatings.
Packaging and delivery:
package:
|
Primer, topcoat, varnish |
20kg/barrel |
|
Thinner |
16kg/barrel |
Supply:
Fulda color card primer, varnish, thinner, topcoat, no order quantity requirements. The minimum supply of topcoats ordered by other companies is 20kg minimum, and the general delivery period is 2-5 days (excluding transportation).