BJ-C220 Series Acrylic Acid Polyurethane Coatings for Engineering Machinery

Description

Introduction:

BJ-C220 Series Acrylic Acid Polyurethane Coating for engineering and Machinery, a kind of cold curing coating, are confected from high quality hydroxy-acrylic resin, modified resin, isocyanic ester without yellow change, weathering resistance pigment and filling, accessory ingredient, solvent by Shanghai Fuleda Fluorocarbon coating Fluorocarbon Material Co. Ltd.. They are packed in two components, namely component A and component B. They are used for the decoration and protection of the surface of engineering machineries.

Application Fields:

Engineer machineries, such as excavator, transport vehicle, crane, bulldozer and pavement roller etc.

Technological Parameters:

Name

Base coat

Top coat

Finish coat

Product No.

BJ-C220

BJ-C220

BJ-C220

Appearance

White and light grey

Colors of all kinds

Transparent color

Fineness

≤30μm

≤25μm

≤25μm

Solid content(Wt%)

≥50%

Metal and pearly luster≥35%,Solid≥50%

≥35%

Drying time

表干≤1h,实干≤24h

Mixing proportion ( A: B)

8:1

Working life

8h

Thinner

X-6 thinner

 

BJ-C Series Coatings Performance

Performance and quality

Standard

Performance Acrylic Acid and Polyurethane Coating

Color

 

Various colors like solid color pearlylustre color, and metallic color

60℃ luster

GB/T 9754-1988

Low, moderate and high luster

Film thickness(photopolymer)

 

Top coat 20-25μm,finishing coat 10-15μm

Hardness(pencil)

GB/T 6739

Minimum H

Adhesion

GB/T 9286-1998

100/100

Impact toughness resistance

GB/T 1732-1993

No motion

Toughness T bend

 

3T

Temperature resistance

 

-40-150℃

Resistance to solvent

Xylene

 100times without appearance of grounding

Salt-spray resistance

GB/T 1771-1991

Meet or exceed the standard in 500 hours

Acid resistance

GB/T 9274-1988

10%HCL15min making no difference

Alkali resistance

GB/T 9274-1988

10%NaOH 1h making no difference

Resistance to laundering

GB/T 1733-1993

making no difference

Weatherability(Sunlight acceleration)

GB/T 1865-1997

Luster loss less than 30% in 1000 hours

Color variation no more than 2NBS

 

Material, Color and Texture:

The main film-forming resin of BJ-C series resin coatings adopts high quality acrylic acid and polyester resin.

Weathering resistance inorganic pigment, import metallic and pearlescent pigment which are applicable to FJ-C are adopted.

At present, BJ-C Series Resin Fluorocarbon Coatings have solid color, metallic color, pearly color and color with other different glass.

Packing and Supply:

Package:

Base coat, top coat, finish coat

20kg/barrel

Thinner

16kg/barrel

 

Supply:

The order quantity for top coat, finishing paint, thinner, whose color are based on the color chart from Shanghai Fuleda Fluorocarbon Material Co., Ltd., are not specified. The minimum monochromic supply for top coat ordered based on other companies sample is 20kg, and the delivery time of BJ-C220 Series Resin Coating is usually 2-5 days.